TEOS-PDMS-calcium oxalate hydrophobic nanocomposite for protection and stone consolidationTEOS-PDMS-calcium oxalate hydrophobic nanocomposite for protection and stone consolidation Peer-Reviewed Journal Publication Δημοσίευση σε Περιοδικό με Κριτές 2023-04-042021enThis work has been supported by the InnovaConcrete project funded by the European program Horizon 2020 (GA No. 760858).A treatment for both protection and consolidation, was synthesized in a simplified procedure through the sol gel process. Synthesized nano-calcium oxalate (CaOx) was incorporated into tetraethoxysilane (TEOS) and polydimethylsiloxane (PDMS), providing a hybrid hydrophobic consolidant nanocomposite. Oxalic acid was selected due to its ability to catalyse the hydrolysis of TEOS, as a drying control agent, but also because of its contribution at the formation of the calcium oxalate in reaction with calcium hydroxide. CaOx, incorporated into the silica matrix of the final copolymer, exhibits interfacial compatibility with the stone substrate and simultaneously strengthens the treated surface, since CaOx appears to be more stable than calcium carbonate. The hydrolysis of TEOS, as well as the formation of CaOx was evaluated through thermogravimetric analysis (TG/DTA). The nanocomposite consists of particles with approximately 7–700 nm in size range, as shown in TEM images. The consolidation, in combination with the hydrophobicity of surface resulted in an increase of the resistance to decay. Mechanical properties were enhanced as evaluated by ultrasonic pulse velocity on treated and untreated surfaces. Furthermore, water contact angle, as well as water absorption by capillarity test, showed improved water repellency of treated stones. Finally, this treatment doesn’t alter the aesthetic surface parameters, a fact that is essential in cultural heritage conservation, while the consolidant remains intact under UV and moisture exposure.http://creativecommons.org/licenses/by/4.0/Heritage444068–4075Maravelaki_et_al_Heritage_4(4)_2021.pdfChania [Greece]Library of TUC2023-04-04application/pdf3.0 MBfree Maravelaki Pagona Μαραβελακη Παγωνα Kapetanaki Kali Καπετανακη Καλη Stefanakis Dimitrios MDPI Stone impregnation Hydrophobic nanocomposite TEOS-calcium oxalate consolidant