Production of ceramics from laterite leaching residues and fayalitic slags

Tsiftsis Vasileios

Simple record


URIhttp://purl.tuc.gr/dl/dias/0A167C7D-0AE2-40B7-8006-85F3B1EDE4B8-
Identifierhttps://doi.org/10.26233/heallink.tuc.84788-
Languageel-
Extent87 σελίδεςel
TitleΠαραγωγή κεραμικών από υπολείμματα εκχύλισης λατερίτη και φαϋαλιτικής σκωρίαςel
TitleProduction of ceramics from laterite leaching residues and fayalitic slagsen
CreatorTsiftsis Vasileiosen
CreatorΤσιφτσης Βασιλειοςel
Contributor [Thesis Supervisor]Komnitsas Konstantinosen
Contributor [Thesis Supervisor]Κομνιτσας Κωνσταντινοςel
Contributor [Committee Member]Galetakis Michailen
Contributor [Committee Member]Γαλετακης Μιχαηλel
Contributor [Committee Member]Kritikaki Annaen
Contributor [Committee Member]Κρητικακη Ανναel
PublisherΠολυτεχνείο Κρήτηςel
PublisherTechnical University of Creteen
Academic UnitTechnical University of Crete::School of Mineral Resources Engineeringen
Academic UnitΠολυτεχνείο Κρήτης::Σχολή Μηχανικών Ορυκτών Πόρωνel
Content SummaryH διπλωματική εργασία παρουσιάζει την παραγωγή και μελέτη κεραμικών και υαλοκεραμικών υλικών από βιομηχανικά απόβλητα, συγκεκριμένα από φαϋαλιτική σκωρία από κάμινο πλάσματος και από υπολείμματα ατμοσφαιρικής εκχύλισης λατερίτη με χρήση θειϊκού οξέος. Τα κεραμικά και υαλοκεραμικά παράχθηκαν με την μέθοδο της ξηρής συμπίεσης και πύρωσης σε τέσσερις θερμοκρασίες 900, 1000, 1100 και 1200 °C και 700, 800, 850 και 900 °C αντίστοιχα. Τα αρχικά υλικά και τα παραχθέντα προϊόντα αναλύθηκαν ως προς την χημική και ορυκτολογική τους σύσταση, με τεχνικές XRF, XRD, και FT-IR. Προσδιορίστηκαν επίσης ιδιότητες όπως το πορώδες, η πυκνότητα, η υδατοαπορροφητικότητα, η αντοχή σε μονοαξονική θλίψη και σε κάμψη, η μικροσκληρότητα και ο συντελεστής θερμικής διαστολής. Επίσης, πραγματοποιήθηκαν δοκιμές θερμικής καταπόνησης, ψύξης και απόψυξης, αντίστασης σε χημική διάβρωση (HCl, KOH) και τοξικότητας. Τα αποτελέσματα κρίνονται πολύ ικανοποιητικά και τα παραγόμενα υλικά μπορούν να χρησιμοποιηθούν σε πολλές εφαρμογές.el
Content SummaryThis diploma thesis investigates the production of ceramics and glass-ceramics from industrial wastes, namely from a fayalitic slag derived from a plasma furnace and laterite leaching residues; laterite leaching was carried out at atmospheric conditions with the use of sulphuric acid. Ceramics and glass-ceramics were produced after compaction of dry powder and roasting at temperatures 900, 1000, 1100, 1200 °C and 700, 800, 850, 900 °C respectively. The raw materials and all products were analyzed chemically and mineralogically using XRF, XRD and FT-IR techniques. Properties such as porosity, density, water adsorption, compressive and tensile strength, microhardness and coefficient of thermal expansion. Also, their toxicity and structural integrity were assess through firing, freeze-thaw cycles and immersion in corrosive media. The results are promising and thus the produced products can be used in a number of applications. en
Type of ItemΔιπλωματική Εργασίαel
Type of ItemDiploma Worken
Licensehttp://creativecommons.org/licenses/by-sa/4.0/en
Date of Item2020-02-27-
Date of Publication2020-
SubjectΚεραμικάel
SubjectCeramicsen
SubjectΦαϋαλιτική σκωρίαel
SubjectGlass-ceramicsen
SubjectΥαλοκεραμικάel
SubjectΥπολείμματα εκχύλισης λατερίτηel
Bibliographic CitationΒασίλειος Τσιφτσής, "Παραγωγή κεραμικών από υπολείμματα εκχύλισης λατερίτη και φαϋαλιτικής σκωρίας", Διπλωματική Εργασία, Σχολή Μηχανικών Ορυκτών Πόρων, Πολυτεχνείο Κρήτης, Χανιά, Ελλάς, 2020el
Bibliographic CitationVasileios Tsiftsis, "Production of ceramics from laterite leaching residues and fayalitic slags", Diploma Work, School of Mineral Resources Engineering, Technical University of Crete, Chania, Greece, 2020en

Available Files

Services

Statistics